Effect of carbonate formation on the physical, mechanical, and fire resistance properties of CaCO3-mineralized sengon wood

Summary

No reviewed summary yet. Read the abstract below or open the original publication.

Abstract

Fast-growing sengon wood falls into the low durability and strength class. Enhancing the physical, mechanical, and fire-resistance properties of sengon can be an important step toward increasing its market value. This study aimed to determine the effectiveness of CaCO3 formation in enhancing physical, mechanical, and fire-resistance properties of sengon wood. The wood was impregnated in two steps with calcium chloride (CaCl2) and assisted potassium carbonate (K2CO3) at three concentrations (0.5, 1, and 2 mol/L). The results showed that the consequent CaCO3 mineralization process at moderate concentrations improved wood properties. The concentrations of 0.5 and 1 mol/L showed optimal overall performance in improving the properties of sengon wood, with 0.5 mol/L offering potential advantages in terms of treatment efficiency. In particular, mechanical properties were increased by about 20% compared to the control. The use of CaCO3 at 2 mol/L was less effective at improving mechanical properties. However, the physical and fire resistance properties were comparable to those of moderate concentrations of 0.5 mol/L and 1 mol/L. Based on this work, mineralization can be regarded as an alternative to improve wood properties, especially fire resistance, for environmentally friendly structural applications.

Abstract as supplied by the source. Full text may be restricted by the publisher.