Characterization, pretreatment, and valorization of wood biomass fly ash in a binary cement-free binder

Xuhui Liang, Hua Dong, Zhenming Li, Chen Liu, Shizhe Zhang, Guang Ye

27 June 2025 · Developments in the Built Environment

Original publication Open Access copy Save

Summary

No reviewed summary yet. Read the abstract below or open the original publication.

Abstract

This research investigated the use of wood biomass fly ash (WBFA) as a key component in developing low-carbon cementitious materials. WBFA was first subjected to water pretreatment and grinding to remove metallic aluminum and free lime, reducing expansion and cracking risks. Characterization of WBFA showed its high calcium and alkali-bearing phases but limited aluminosilicates. Dissolution test showed WBFA had strong alkalinity, suggesting its role as an activator for aluminosilicate-bearing minerals. A novel cement- and chemical-free binary binder was developed using 50% treated WBFA and 50% blast furnace slag (BFS). Paste with a water-to-binder ratio of 0.4 achieved 40 MPa compressive strength at 60 days. The use of superplasticizer significantly improved flowability, allowing the water-to-binder ratio to be reduced to 0.25, which resulted in compressive strengths up to 58 MPa at 60 days. Calcium aluminate silicate hydrates (C-A-S-H) gels and ettringite were identified as the main reaction products in the pastes.

Abstract as supplied by the source. Full text may be restricted by the publisher.