Durability, mechanical properties, and fire resistance of wood impregnated with dilute alumino-silicate suspensions at different pH levels

Summary

No reviewed summary yet. Read the abstract below or open the original publication.

Abstract

This study evaluates the effects of dilute alumino-silicate suspension (uncured geopolymer dilution) impregnation on Pinus sylvestris sapwood, focusing on pH adjustments. Higher concentrations of the alumino-silicate suspensions (3% and 5%) led to a statistically significant improvement in decay resistance, with all treated samples exhibiting mass losses between 2.2 ± 0.6% and 5.8 ± 1.6%— approximately half of that observed for the untreated controls (9.9 ± 2.4%). In contrast, pH adjustments had only a minor effect. The lowest concentration of dilute alumino-silicate suspensions did not significantly enhance decay resistance, although the mass loss was slightly higher than that of the controls. Mechanical tests showed that intermediate concentrations of alumino-silicate suspensions improved the modulus of elasticity (MOE) and modulus of rupture (MOR), while fire resistance tests indicated an improvement in ignition time of up to 5 s at 5% alumino-silicate suspension. The leaching test revealed challenges with the fixation of the dilute alumino-silicate suspensions, resulting in reduced durability after prolonged water exposure. These findings underscore the potential of dilute alumino-silicate suspensions as sustainable wood treatments. However, further optimization of their formulations is required to enhance adhesion and reduce leachability.

Abstract as supplied by the source. Full text may be restricted by the publisher.