Influence of drying methods before thermal modification on the mechanical properties of oak sawn timber

Summary

No reviewed summary yet. Read the abstract below or open the original publication.

Abstract

This study investigated the influence of three drying strategies – conventional kiln, radio-frequency/vacuum with mechanical press (RF/VP), and hot-air/vacuum drying – on the mechanical properties of oak sawn timber after vacuum heat treatment at 190°C and subsequent superheated steam conditioning. Mechanical performance was evaluated through bending, compressive, and tensile tests across different processing stages. Hot-air/vacuum drying showed the highest strength after heat treatment (bending: 131 MPa, compressive: 86 MPa, tensile: 113 MPa) and after conditioning (bending: 104 MPa, compressive: 83 MPa, tensile: 100 MPa), outperforming conventional kiln drying (74/71 MPa, 81/78 MPa, and 57/53 MPa), highlighting its potential as the most effective strategy. Although RF/VP drying increased density, it did not translate into proportional strength benefits, which is likely attributable to microstructural deformation and residual stress induced by high compressive loading during RF/VP drying, indicating that density alone is not a reliable indicator of structural integrity in thermally modified wood. These results demonstrate that drying history critically shapes the mechanical outcomes of heat-treated oak. Hot-air/vacuum drying, in particular, enables improved strength retention and recovery, offering practical guidelines for producing durable, high-performance hardwood products. The findings provide insights for optimising drying and post-treatment protocols to balance efficiency and mechanical performance in modern wood processing.

Abstract as supplied by the source. Full text may be restricted by the publisher.